One of the opportunities at innocentives is 20k USD to a person that comes up with a way to keep candy from bouncing against candy affecting the surface appearance.
About my third idea was Prince Ruperts candy, the prince rupert effect is where as a result of overlaying stresses a blob is basically
nondestructible unless you apply force to just one particular area. So, is there a way to do this to candy, to prestress the coating so it is nondestructible. Could a mathematician model a container that was prestressed so as to be nondestructable, then fill it with gooey candy. sort of like W &Ws
Now some people here will say, if it works that well, what about the people that try to eat it. My hope is that dissolving or warmth would modify the prince rupert effect.
It could also be possible to coat candy with micro princess ruperts structures so the candy might appear microglittery or even velvety yet the superstrong surface would reduce scuffing.
It is possible that making candy bubbles at an ultrasonic chamber could produce a rupertesque effect at the W&W like candy surface prior to putting the goop at the center
One idea that I think many people must have thought of is covering the candy with a material that goes directly from crystal to gas, then just printing a (do not use prior to) date on the package to be sure the coating turns to gas prior to being eaten. One chemical as well as physical variant of that that may actually function is to make a rice krispy, aerogel, or microlattice of a natural product, now many people are aware that camphor evaporates, yet I think vanillin crystals also evaporate, thus something that was .995 air .005 vanillin, or a slightly modified chemical similar, yet scentless, might actually be a harmless surface coating that actually evaporated, with a pleasant flavor or no flavor as a residue. So, coat them with edible aerogel that evaporates or, create tiny little aerogel fluffy blobs that interstitially surround the candy then evaporate.
microlattice is currently .999 air, or five times less massive than aerogel (link)
Other ideas were that they could jostle confections at a variety of frequencies to see which frequencies made it through the packaging, notably transport packaging causing the variation. Then create a vibration absorbing bulk packaging that absorbed that. It seems possible that acoustic node active vibration removal as is being tried at cars could certainly be applied to transport trailers as a thing of benefit to more than just W&Ws
Innocentives is a site where they financially reward people that solve technological opportunities sponsors present. I do not have the kind of mind that can participate, also all my ideas are public domain, thus the .5b gets the casual innocentive solution
innocentive prizes given to functional ideas
http://www.innocentive.com/ among many other things, 372 people making an effort to create scuffless candy currently on the front page. With 372 people working on this I think all three of these ideas must have been suggested [beanangel, Feb 29 2012]
nanomesh, which I call microlattice is lighter tha aerogel
http://www.dailytec...am/article23318.htm [beanangel, Feb 29 2012]
Princess Ruperts effect
http://www.en.wikip...rince_Rupert's_Drop [beanangel, Feb 29 2012, last modified Mar 01 2012]
Please log in.
If you're not logged in,
you can see what this page
looks like, but you will
not be able to add anything.
Annotation:
|
|
[+] because Prince Rupert drops are cool. But are
they as robust against grinding as against
hammering? I have a notion that making a tiny
scratch in the surface of a drop (e.g. by rubbing it
against something of equal hardness) is one of the
ways to make it go "poof." |
|
|
Why not work on candies that resemble classical
Prince Rupert drops, not for scuff-prevention, but
as a gimmick: biting down on one would be an
interesting experience. |
|
|
[beanangel], I'm so relieved; after your last post, I was
afraid you'd gone sane. |
|
|
so I am wondering what the other 371 ideas about how to accomplish this are, if each person has their own idea. |
|
|
like im sure there are CVD diamond candies suggested, maglev centers, long dispensers where you shake the candy out of an aperture yet the shaking process produces the coating, microfiber sprays on the surrounding packaging, vacuum linked corduroy velvets that keep each candy suctioned to a soft area until the container is opened, coatings that melt then re harden smooth at 100 degrees combined with each candy being containerized, negative contact angle sugar crystals, shape memory coatings, |
|
|
Why do you say that; //I do not have the kind of mind that can participate// beanangel? |
|
|
Sounds like you have several ideas. |
|
|
/ jostle confections at a variety of frequencies to see which frequencies made it through the packaging, notably transport packaging causing the variation./ |
|
|
I like that one. Iteration, trial and error, clear solution. |
|
|
Bean I pitch crap at innocentive all the time. You should too, because why not? It is less educational because of the lack of community but still sometimes fun. |
|
|
I have also been very curious about what all the other schemes are. I suspect the nonwinning schemes are kept secret because business model for Innocentive means the sponsor gets all the halfbaked alsoran ideas to think about and the competition does not. |
|
|
I am more than a little spoiled by the halfbakery. |
|
|
You people are very kind, actually innocentives just has this word that starts with p that I carefully avoid |
|
|
anyway, perhaps people here will have fun with candy, innocentives or both |
|
|
Looked at the i site; apart from a plethora of stuff I couldn't understand, could only find two that interested me, but the one: "reduce friction" isn't clear as to whether it's loaded or unloaded contact (my idea will work quite well on one but on the other be an almost total waste of time), and the two 'magically find database inconsistencies', the blurb author seems to think "anomaly" and "error" are synonymic. |
|
|
I think it would be an interesting experiment to have bean submit a graduate thesis paper just to see what the profs would write back. |
|
|
The strain-hardening of the Prince Rupert effect is precisely why drinking glasses typically have a bead around their rim. |
|
| |