Even melted pewter is dangerous but what if your kids could work with metal which turns liquid at 70 C and solidifies instantly at room temperature?
Wood's metal conforms to these requirements. The difference is that the mold itself would need to be heated rather than the metal.
The child would
pour granulated Wood's metal into an already heated mold until a puddle forms at the top.
Previous creations can be easily re-granulated for future "pours".
Safe, except ...
https://www.flinnsc...known%20carcinogen.
[pertinax, Jun 06 2024]
"Now Benzene-free!"
_22Now_20Benzene_20free!_22_20stickers
[hippo, Jun 06 2024]
£153 for 500g - not bad
https://www.ebay.co...=artemis&media=COPY
[hippo, Jun 06 2024]
Copper crisis!
https://www.cruxinv...ens-electric-future
...hopefully more real than the climate crisis. [2 fries shy of a happy meal, Jun 13 2024]
Please log in.
If you're not logged in,
you can see what this page
looks like, but you will
not be able to add anything.
Destination URL.
E.g., https://www.coffee.com/
Description (displayed with the short name and URL.)
|
| |
Or you could just use lead. I'm sure the dangers of breathing in the fumes from boiling lead are exaggerated. |
|
| |
You could promote the relative safety of lead fumes by comparing them to mercury fumes. The infographics just draw themselves. |
|
| |
[+] in memoriam [8th of 7], for his known feelings about children. |
|
| |
[pertinax] Indeed! The marketing for this kit will say "Now Mercury-free!" |
|
| |
Or you could just use wax. I really think a children's "Make your own wax cylinder" kit would sell well. It would have a mould for the wax cylinder and a supply of wax pellets to melt down, a hand-cranked thing to turn the cylinder and instructions on finding your own rose thorn for the needle, making a paper cone for the sound reproduction, and also instructions for recording and playback |
|
| |
True - although while Field's metal is "less toxic", it's also not "safe for children" |
|
| |
//I don't think any metal in this category will be safe for children. Conducts heat too rapidly so it can burn careless fingers.// |
|
| |
xenzag mentioned gallium. Melting at around 30°C (86°F), you can melt it in your hand, and the metallic form at least is pretty much non-toxic. |
|
| |
Ideally, I think you'd ideally want a slightly higher melting point, so your castings wouldn't liquify on a warm summer's day. It would probably be possible to make an alloy with other relatively non-toxic metals (maybe tin?) with a melting point of 44°C or so; that should be pretty safe. |
|
| |
Of course, you'd still need to keep it away from aluminium and steel, gallium does tend to knacker those. |
|
| |
Well crap, I didn't know it was toxic. |
|
| |
The whole heating the mold rather than making the metal a liquid first and then pouring?
Has it been done before? |
|
| |
You'd probably need to melt the material before it went into the mould anyway. Otherwise, there will be too many bubbles and the cast quality will be shite. |
|
| |
Heating the mould for metal casting is I think standard for many processes. I've seen people do it in amateur small-scale casting videos on youtube. |
|
| |
If you have pellets, there is air between them.
Bubbles are the bane of casting things. You really don't want to be trying to deal with air inside your mould - especially not when it's hot and full of liquid metal. |
|
| |
Once you start shaking something heavy and hot enough to cause third degree burns around, I'm not sure 'safe' is the appropriate word. |
|
| |
n.b. what does third-degree burn mean?
This text is provided as a courtesy to the squeamish, last chance to look away... First degree is 'superficial', appears red with blisters, healing time 5-10 days. Forth degree is 'black and charred'; does not heal. Third degree is a full skin thickness burn, healing is prolonged and incomplete. This is a little more padding text. |
|
| |
You guys are the rocket-surgeons... |
|
| |
...I just relay brain-farts which may or not be viable. |
|
| |
I'm glad this one seems to maybe have a touch of merit.
They are talking about making citizens sort alcoholic and soda-pop aluminum before refund...
...I would just a soon solar-smelt all of that aluminum down to ingots and bury it. |
|
| |
I've also got about a thousand pounds or so of copper to be recycled. |
|
| |
Should I smelt and sit on it? |
|
| |
I wondered what you guys thought? |
|
| |
What used to be a Simpsons Sears and a Safeway collapsed and I now own them and had to clean them up by hand. They were built in 1984 and "everything" back then was copper. |
|
| |
If you can put yourself in my shoes I would really appreciate feedback. |
|
| |
This whole fake-it til you make-it thing is over-rated. |
|
| |
Some feedback from people who actually 'know' history... |
|
| |
I'm about as out of my depth as I've ever been and, any advice is appreciated. |
|
| |
Just got here, and I don't have much to contribute, but as John Varley said "Mumble". |
|
| |
I envy your copper collection - smelting takes energy though. Large pieces could be used to build stills - And you should read up on sand casting also, I've got sand casting fantasies about making sculptures that I'll probably never realize, such as using firearms or fish to make molds. For that matter, if you are feeling creative, soldering or welding scrap in interesting shapes could be fun. |
|
| |
And, of course, selling scrap metals for cash is nice. Depending on how corroded your stash is, prices will vary. |
|
| |
//Should I smelt and sit on it?// |
|
| |
Short answer, I'd say no. |
|
| |
If you want to hold commodities as a hedge against inflation, then you would probably be better off with more liquid commodities (that is, ones that are easier to buy and sell, because you can find more buyers and sellers for, say, gold, without having to drive a truckload of stuff to Chicago). |
|
| |
If you want to hoard stuff in preparation for the collapse of civilisation, then conversion into ingots is probably not going to add much value, because you're going to need to reconvert it later to some other form. |
|
| |
If you want to speculate on the future price of copper and aluminium, with a view to selling later, then that price depends on how much governments around the world prioritize decarbonisation; the harder they try to decarbonise, the higher goes the price of Cu and Al, but then you're gambling on the results of various elections, and "unknown unknown" future events and, while you're waiting for the price to go up (it's currently going down), your assets are not yielding any income. |
|
| |
So, I'd suggest
1. making things (see suggestions from [normzone]), because making things is something you can probably do better than most people. And
2. if you have too much material ever to use up that way, then I'd suggest trying to identify other people within a convenient distance of where you live, who also make stuff out of metal, and seeing what sort of deals you can make with them. Whether or not you make much money, those relationships might come in handy later. And then
3. if you still have a whole lot left over, see if you can find someone you trust in the local scrap metal market. |
|
| |
I don't know if that advice is of any use to you - but, since you asked for advice, that's how it looks to me. |
|
| |
There is talk of a copper crisis looming, [link], so I do believe I will keep every wire longer than 50 feet and decouple any intact pipe.
The remainder I will sell for scrap later when it equals the price of one ounce of gold. |
|
| |
I do like the idea of making a sculpture from it though.
It would turn all green like the Statue of Liberty.
I once took a year and built a bobble-headed dragon hanging from a string. I would someday like to recreate that from stronger materials than the first time.
The original was made from tin and its head bobbled from the first neck segment which bobbled from the second neck segment... etc. I think there were five or so. The wings actually, flapped counter balanced by the feet. The feet held a tea-candle in a blue glass holder. The tail acted like one of those plastic snakes which strike outwards when tilted slightly. |
|
| |
I made a heat engine of a bi-metalic strip from a thermostat on a teeter-totter to contract when entering the flame of the candle and strike the cords inside the body which would cause it to appear to come to life when the candle was lit. |
|
| |
I wasn't able to build it small enough to fit inside the sculpture but picture a reflective metallic dragon with orange and blue ripples playing over its scales as it languidly flaps while it slowly looks around the room in all directions, tail swishing serenely behind. |
|
| |
It was pretty cool before our postal service pulled an Ace Ventura and destroyed it.
"Gotta package people!" |
|
| |
This one I buy. I told you guys that precious metals were next on the auction block. |
|
| |